Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.22 -- |
| Water absorption rate | | % | 1.5 -- |
| Water absorption rate | | % | 5.0 -- |
| Shrinkage rate | | % | 0.10 -- |
| Shrinkage rate | | % | 0.40 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | MPa | 130 90.0 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 10 12 |
| Charpy Notched Impact Strength | | kJ/m² | 9.0 9.0 |
| Impact strength of simply supported beam without notch | | kJ/m² | 40 45 |
| Impact strength of simply supported beam without notch | | kJ/m² | 35 35 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | % | 3.0 5.0 |
| tensile strength | Break | MPa | 110 90.0 |
| Tensile modulus | | MPa | 6900 5200 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| dielectric strength | | kV/mm | 40 34 |
| Volume resistivity | | ohms·cm | 1E+14 1E+11 |
| Surface Resistivity | | ohms | -- 1E+12 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.5E-04 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 2.5E-05 -- |
| melting temperature | | °C | 222 -- |
| Continuous use temperature | | °C | 160 -- |
| Continuous use temperature | | °C | 80.0to110 -- |
| Heat distortion temperature | | °C | 70.0 -- |
| Heat distortion temperature | | °C | 155 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.