PA66 A 60G1 V30 SOLVAY FRANCE

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	85	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8 mm	UL 94	V-0
	UL flame retardant rating	1.6 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.2 mm	UL 94	V-0
Burning wire flammability index	0.8 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.6 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.2 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.8 mm	IEC 60695-2-13	775	°C
Extreme Oxygen Index		ISO 4589-2	33	%
European Railways Certifications	R22	EN 45545-2	HL3
European Railways Certifications	European Railways Certifications	R23	EN 45545-2	HL3
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1A	10200	Mpa
tensile strength	Break, 23°C	ASTM D638	140	Mpa
tensile strength	tensile strength	Break, 23°C	ISO 527-2/1A	150	Mpa
elongation	Break, 23°C	ASTM D638	3.0	%
elongation	elongation	Break, 23°C	ISO 527-2	2.3	%
Bending modulus	23°C	ASTM D790	10000	Mpa
bending strength	23°C	ASTM D790	225	Mpa
bending strength	bending strength	23°C	ISO 178	255	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Suggested maximum moisture content			0.20	%
Temperature at the rear of the barrel			265 to 275	°C
Temperature in the middle of the barrel			265 to 275	°C
Temperature at the front of the material cylinder			270 to 280	°C
Mold temperature			60 to 90	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	245	°C
Melting temperature		ISO 11357-3	263	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183/A	1.46	g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.0	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.35	%
Water absorption rate	24 hr, 23°C	ISO 62	0.73	%
	Water absorption rate	Saturation, 23°C	ISO 62	4.3	%
	Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.8	%
Outdoor applicability	全部	UL 746C	f1
Thermogravimetric analysis (TGA)	1%失重温度	NF F16-101	I3
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	6.0E+14	ohms·cm
Dielectric strength	0.800 mm	IEC 60243-1	38	KV/mm
Compared to the anti leakage trace index	Solution A	IEC 60112		V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.