Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.39 g/cm³ |
| Shrinkage rate | | 内部方法 | 1.5 % |
| Water absorption rate | | ASTMD570 | 0.90 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTMD2863 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTMD790 | 100 MPa |
| tensile strength | Yield | ASTMD638 | 60.0 MPa |
| elongation | Break | ASTMD638 | 10 % |
| Flexural modulus | | ASTMD790 | 2750 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+03 ohms·cm |
| dielectric strength | | ASTMD149 | 19 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 200 °C |
| Heat distortion temperature | | ASTMD648 | 80.0 °C |
| melting temperature | | ISO 1218 | 220 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.