Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 1.4 g/10min |
| melt mass-flow rate | | ISO1133 | 1.3 g/10min |
| viscosity number | | ISO307 | 600 cm³/g |
| intrinsic viscosity | | ISO1628-3 | 6.0 dl/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 63 |
| | ISO868 | 63 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1A/1 | 1100 Mpa |
| Tensile stress | | ISO527-2/1A/50 | 26.0 Mpa |
| Tensile strain | | ISO527-2/1A/50 | 9.0 % |
| Nominal tensile fracture strain | | ISO527-2/1A/50 | >50 % |
| Tensile creep modulus | | ISO899-1 | 680 Mpa |
| Tensile creep modulus | | ISO899-1 | 340 Mpa |
| WearbySandslurryMethod3 | | 内部方法 | 310 |
| Wear amount | | 内部方法 | 250 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| CharpyImpactStrength4 | | ISO1152-2 | 25.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | >1.0E+13 ohms |
| Surface Resistivity | | IEC60093 | >1.0E+12 ohms |
| Volume resistivity | | ASTMD257 | >1.0E+15 ohms·cm |
| Volume resistivity | | IEC60093 | >1.0E+14 ohms·cm |
| dielectric strength | | IEC60243-1 | 40 KV/mm |
| dielectric constant | | ASTMD150 | 2.90 |
| dielectric constant | | IEC60250 | 2.00 |
| dielectric constant | | IEC60250 | 2.00 |
| Dissipation Factor | | IEC60250 | 2E-04 |
| Dissipation Factor | | IEC60250 | 4E-04 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD696,ISO11359-2 | 2E-04 cm/cm/°C |
| specific heat | | 内部方法 | 1840 J/kg/°C |
| thermal conductivity | | 内部方法 | 0.41 W/m/K |
| | ISO75-2/B | 75.0 °C |
| | ISO75-2/A | 41.0 °C |
| vicat | | ASTMD1525,ISO306/B50 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.