Technical Data Sheet
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527 | 9.00 MPa |
| elongation | Break | ISO 527 | 210 % |
| dielectric strength | | IEC 60243 | 23 kV/mm |
| Shore hardness | | ISO 868 | 75to80 |
| Volume resistivity | | IEC 60093 | 4E+14 ohms·cm |
| relative permittivity | | IEC 60250 | 3.00 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | | 0.50 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 1200to2000 cP |
| Thermosetting components | Resin | | 100 |
| Thermosetting components | | | 5.0to30 min |
| Thermosetting components | Hardener | | 按重量计算的混合比:26 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.06to1.09 g/cm³ |
| density | | | 1.20to1.24 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| operate temperature | | | -60-125 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | TMA | -60.0 °C |
| thermal conductivity | | ISO 22007-2 | 0.30 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.