Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.36 % |
| Water absorption rate | | ASTM D570 | 0.45 % |
| density | | ASTM D792 | 1.39 g/cm³ |
| Apparent density | | ASTM D1895 | 0.60 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 90 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ASTM D2863 | 25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 9010 MPa |
| tensile strength | | ASTM D638 | 58.0 MPa |
| elongation | Break | ASTM D638 | 0.70 % |
| Flexural modulus | | ASTM D790 | 8770 MPa |
| compressive strength | | ASTM D695 | 215 MPa |
| bending strength | | ASTM D790 | 96.4 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ASTM D256 | 19.2 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 20 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 0.038 |
| arc resistance | | ASTM D495 | 103 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 |
| Volume resistivity | | ASTM D257 | 5.7E+12 ohms·cm |
| dielectric strength | | ASTM D149 | 14 kV/mm |
| dielectric constant | | ASTM D150 | 4.60 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 172 °C |
| Continuous use temperature | | ASTM D794 | 196 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 6.8E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.37 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.