| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.41 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 1.3 % |
| Shrinkage rate | | ISO 294-4 | 0.50 % |
| Water absorption rate | | ISO 62 | 2.6 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10, -20 | HB |
| Flammability level | | IEC 60695-11-10, -20 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 10000 Mpa |
| Tensile modulus | | ISO 527-2 | 5500 Mpa |
| Tensile modulus | | ISO 527-2 | 5000 Mpa |
| Tensile modulus | | ISO 527-2 | 4400 Mpa |
| Tensile modulus | | ISO 527-2 | 4000 Mpa |
| Tensile stress | | ISO 527-2 | 210 Mpa |
| Tensile stress | | ISO 527-2 | 110 Mpa |
| Tensile stress | | ISO 527-2 | 100 Mpa |
| Tensile stress | | ISO 527-2 | 95.0 Mpa |
| Tensile stress | | ISO 527-2 | 90.0 Mpa |
| Tensile strain | | ISO 527-2 | 4.0 % |
| Tensile strain | | ISO 527-2 | 7.5 % |
| Tensile strain | | ISO 527-2 | 7.5 % |
| Tensile strain | | ISO 527-2 | 7.5 % |
| Tensile strain | | ISO 527-2 | 7.5 % |
| Flexural modulus | | ISO 178 | 9000 Mpa |
| Flexural modulus | | ISO 178 | 4700 Mpa |
| Flexural modulus | | ISO 178 | 3900 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 11 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 65 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 80 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 11 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 35 KV/mm |
| | IEC 60250 | 4.40 |
| | IEC 60250 | 4.00 |
| CTI | | IEC 60112 | 500 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 290 °C |
| Heat distortion temperature | | ISO 75-2/A | 290 °C |
| Melting temperature 3 | | ISO 11357-3 | 295 °C |
| | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| | ISO 11359-2 | 6.0E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 65.0 °C |
| Thermal Index - 5000 hr | | IEC 60216 | 152 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.