Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792,ISO1183 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO1133 | 12 g/10min |
| Shrinkage rate | | 内部方法 | 1.8到2.2 % |
| Water absorption rate | | ASTMD570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 92 |
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 85 J/m |
| Charpy Notched Impact Strength | | ISO179 | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2900 MPa |
| Tensile stress | Yield | ISO527-2 | 68.0 MPa |
| Tensile stress | | ASTMD638 | 67.0 MPa |
| elongation | Break | ASTMD638,ISO527-2 | 45 % |
| Flexural modulus | | ASTMD790 | 2800 MPa |
| Flexural modulus | | ISO178 | 2700 MPa |
| bending strength | | ASTMD790 | 95.0 MPa |
| | ASTMD1044 | 13.0 mg |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTMD149 | 18 kV/mm |
| arc resistance | | ASTMD495 | 250 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 172 °C |
| Heat distortion temperature | | ISO75-2/B | 155 °C |
| Heat distortion temperature | | ASTMD648 | 125 °C |
| Heat distortion temperature | | ISO75-2/A | 90.0 °C |
| | ASTMD696,ISO11359-2 | 1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.