PA6 TY A218V35 SOLVAY SHANGHAI

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	80	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8 mm	UL 94	HB
	UL flame retardant rating	1.6 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.2 mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	23	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1A	11400	Mpa
tensile strength	Break, 23°C	ISO 527-2/1A	210	Mpa
Tensile strain	Break, 23°C	ISO 527-2	3.0	%
Bending modulus	23°C	ASTM D790	9800	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	9500	Mpa
bending strength	23°C	ASTM D790	290	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Suggested maximum moisture content			0.20	%
Temperature at the rear of the barrel			270 to 280	°C
Temperature in the middle of the barrel			275 to 285	°C
Temperature at the front of the material cylinder			280 to 290	°C
Mold temperature			70 to 100	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	255	°C
Melting temperature		ISO 11357-3	263	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	1.1	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.35	%
Water absorption rate	24 hr, 23°C	ISO 62	0.75	%
	Water absorption rate	Saturation, 23°C	ISO 62	5.4	%
	Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.6	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	6.0E+15	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength	2.00 mm	IEC 60243-1	34	KV/mm
Relative permittivity		IEC 60250	3.70
Dissipation factor		IEC 60250	0.010
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.