Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:60 |
| Thermosetting mixed viscosity | | ASTMD2393 | 1800到2000 cP |
| stripping time | | | 120到180 min |
| Post curing time | | | 72到120 hr |
| Post curing time | | | 4.0到6.0 hr |
| | | 按重量计算的混合比:100 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.10 g/cm³ |
| Specific volume | | | 0.910 cm³/g |
| Shrinkage rate | | ASTMD955 | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 68到72 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WorkLife | | | 18.0到20.0 min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 248 MPa |
| Flexural modulus | | ASTMD790 | 538 MPa |
| bending strength | | ASTMD790 | 25.5 MPa |
| compressive strength | | ASTMD695 | 67.6 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTMD412 | 26.2 MPa |
| elongation | Break | ASTMD412 | 400 % |
| tear strength | | ASTMD624 | 114 kN/m |
| compression set | | ASTMD395B | 72 % |
| Basho elasticity | | ASTMD575 | 48 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.