Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 收缩率 | MD：1.59mm | ASTMD955 | 1.4 % |
| 收缩率 | MD：3.18mm | ASTMD955 | 1.3 % |
| 收缩率 | TD：1.59mm | ASTMD955 | 0.50 % |
| 收缩率 | TD：3.18mm | ASTMD955 | 1.1 % |
| 收缩率 | TD:1.59mm | ISO294-4 | 0.50 % |
| 收缩率 | MD:1.59mm | ISO294-4 | 1.4 % |
| 收缩率 | TD:3.18mm | ISO294-4 | 1.1 % |
| 收缩率 | MD:3.18mm | ISO294-4 | 1.3 % |
| MeltViscosity | 190°C,300sec^-1 | ASTMD3835 | 219 Pa·s |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 脆化温度 | | ASTMD746 | -61.1 °C |
| 脆化温度 | | ISO812 | -61.1 °C |
| 老化 | Test Condition | Test Method | Test Result |
|---|
| 断裂时拉伸应力变化 | 70°C,168hr | ISO1817 | -5.0 % |
| 断裂时拉伸应力变化 | 100°C,168hr | ISO1817 | 4.0 % |
| 体积变化 | 24°C,168hr,inReferenceFuelB | ASTMD471 | 54 % |
| 体积变化 | 100°C,168hr,inASTM#1Oil | ASTMD471 | 6.0 % |
| 体积变化 | 100°C,168hr,inIRM903Oil | ASTMD471 | 82 % |
| 体积变化 | 100°C,168hr,在水中 | ASTMD471 | 1.0 % |
| 体积变化 | 24°C,168hr,inReferenceFuelB | ISO1817 | 54 % |
| 体积变化 | 100°C,168hr,inASTM#1Oil | ISO1817 | 6.0 % |
| 体积变化 | 100°C,168hr,inIRM903Oil | ISO1817 | 82 % |
| 体积变化 | 100°C,168hr,在水中 | ISO1817 | 1.0 % |
| 空气中拉伸强度的变化率 | 70°C,168hr | ASTMD573 | -2.0 % |
| 空气中拉伸强度的变化率 | 100%Strain,70°C,168hr | ASTMD573 | 7.0 % |
| 空气中拉伸强度的变化率 | 100°C,168hr | ASTMD573 | -2.0 % |
| 空气中拉伸强度的变化率 | 100%Strain,100°C,168hr | ASTMD573 | 7.0 % |
| 空气中拉伸强度的变化率 | 70°C,168hr | ISO188 | -2.0 % |
| 空气中拉伸强度的变化率 | 100%Strain70°C,168hr | ISO188 | 7.0 % |
| 空气中拉伸强度的变化率 | 100°C,168hr | ISO188 | -2.0 % |
| 空气中拉伸强度的变化率 | 100%Strain100°C,168hr | ISO188 | 7.0 % |
| 空气中极限伸长率的变化率 | 70°C,168hr | ASTMD573 | -5.0 % |
| 空气中极限伸长率的变化率 | 100°C,168hr | ASTMD573 | 4.0 % |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| TaberAbrasionResistance | 1000Cycles,1.0E+6g,CS-17Wheel | ASTMD1044 | 12.5 mg |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 肖氏硬度 | 邵氏A,5秒 | ASTMD2240 | 78 |
| 肖氏硬度 | 邵氏A,5秒 | ISO868 | 78 |
| 弹性体 | Test Condition | Test Method | Test Result |
|---|
| 拉伸永久变形 | 100%应变 | ASTMD412 | 16 % |
| 拉伸应力 | 100%应变 | ASTMD412 | 2.54 Mpa |
| 拉伸应力 | 100%应变,23°C | ISO37 | 2.54 Mpa |
| 抗张强度 | 屈服,23°C | ASTMD412 | 8.30 Mpa |
| 拉伸应力 | 屈服,23°C | ISO37 | 8.30 Mpa |
| 伸长率 | 断裂 | ASTMD412 | 310 % |
| 伸长率 | 断裂,23°C | ISO37 | 310 % |
| TearStrength2 | 24°C | ASTMD624 | 33.4 kN/m |
| 压缩永久变形 | 24°C,22hr | ASTMD395B | 26 % |
| 压缩永久变形 | 70°C,22hr | ASTMD395B | 48 % |
| 压缩永久变形 | 100°C,22hr | ASTMD395B | 63 % |
| 压缩永久变形 | 24°C,22hr | ISO815 | 26 % |
| 压缩永久变形 | 70°C,22hr | ISO815 | 48 % |
| 压缩永久变形 | 100°C,22hr | ISO815 | 63 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.