Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 0.900 g/cm³ |
| melt mass-flow rate | | ISO1133 | 3.5 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 95 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Gardner glossiness | | ASTMD523 | 90 |
| Haze ratio | | ISO14782 | 20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2 | 32.0 MPa |
| Nominal tensile fracture strain | | ISO527-2 | >400 % |
| Flexural modulus | | ISO178 | 1350 MPa |
| Tensile modulus | | ISO527-2 | 1350 MPa |
| Bending stress | | ISO178 | 40.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 1.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 5.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 95.0 °C |
| vicat | | ISO306 | 130 °C |
| Crystallization peak temperature | | ISO11357-3 | 144 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare