Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.05 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 20to28 g/10min |
| melt mass-flow rate | | ISO 1133 | 5.0 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.40to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 20 % |
| elongation | Break | ISO 527-2/50 | 15 % |
| Flexural modulus | | ASTM D790 | 2400 MPa |
| tensile strength | | ASTM D638 | 72.0 MPa |
| Flexural modulus | | ISO 178 | 2300 MPa |
| bending strength | | ASTM D790 | 90.0 MPa |
| tensile strength | | ISO 527-2/50 | 70.0 MPa |
| bending strength | | ISO 178 | 88.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Impact strength of cantilever beam gap | | ASTM D256 | 260 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 14 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 24 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 25 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 无断裂 |
| Suspended wall beam without notch impact strength | | ISO 180 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+14 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/B50 | 162 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.6E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7.6E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/B | 160 °C |
| Heat distortion temperature | | ASTM D648 | 151 °C |
| Heat distortion temperature | | ISO 75-2/A | 150 °C |
| vicat | | ASTM D15256 | 155 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare