Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.82 g/cm³ |
| Tightening rate | | | 6.0 |
| Shrinkage rate | | | 0.10到0.40 % |
| Dimensional Stability | | | <0.010 % |
| Water absorption rate | | | 0.30 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WaterExtractConductivity | | | 30.0 µS/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 41.4到68.9 MPa |
| bending strength | | | 89.6到117 MPa |
| compressive strength | | | 165到207 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 160到320 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | | 4.20 |
| Dissipation Factor | | | 6E-03 |
| Dissipation Factor | | | 9E-03 |
| Dissipation Factor | | | 0.014 |
| Dissipation Factor | | | 0.016 |
| Dissipation Factor | | | 180 sec |
| DielectricBreakdown | | | 62000 V |
| DielectricBreakdown | | | 60000 V |
| Surface Resistivity | | | >1.0E+16 ohms |
| Surface Resistivity | | | 2.6E+10 ohms |
| Volume resistivity | | | >1.0E+16 ohms·cm |
| Volume resistivity | | | 2E+10 ohms·cm |
| dielectric strength | | | 16 kV/mm |
| dielectric strength | | | 14 kV/mm |
| dielectric constant | | | 4.20 |
| dielectric constant | | | 4.40 |
| dielectric constant | | | 4.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 2.4E-05 cm/cm/°C |
| Heat distortion temperature | | | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.