PP REPRO PP RG4
0
- Properties:Fillerglass fiber reinforced material20%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO1133 | 7.0 g/10min | |
| density | ISO1183 | 1.05 g/cm³ | |
| melt mass-flow rate | ISO1133 | 7.0 g/10min | |
| density | ISO1183 | 1.05 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB | |
| Hot filament ignition temperature | IEC60695-2-13 | 750 °C | |
| UL flame retardant rating | UL94 | HB | |
| Hot filament ignition temperature | IEC60695-2-13 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | ISO527-2 | 30.0 MPa | |
| Flexural modulus | ISO178 | 2900 MPa | |
| Bending stress | ISO178 | 45.0 MPa | |
| Flexural modulus | ISO178 | 2900 MPa | |
| Bending stress | ISO178 | 45.0 MPa | |
| Tensile stress | ISO527-2 | 30.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179 | 7.0 kJ/m² | |
| ISO179 | 7.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO75-2/B | 125 °C | |
| ISO75-2/A | 95.0 °C | ||
| ISO75-2/B | 125 °C | ||
| ISO75-2/A | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.