PC PANLITE® GV-3410R TEIJIN SHANGHAI

Properties:
High rigidityAnti creepFiller: Glass fiber reinf10% filler by weight
Usages:
Industrial applicationsElectrical fieldElectronic fieldIndustrial applicationsElectrical components
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	40 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40mm	UL 94	V-2
	UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	3800 Mpa
bending strength		ISO 178	125 Mpa
Tensile modulus		ISO 527-2/1	3900 Mpa
tensile strength	Break	ISO 527-2/5	75.0 Mpa
Tensile strain	Break	ISO 527-2/5	3.5 %

thermal performance	Test Condition	Test Method	Test Result
RTI Imp	1.5mm	UL 746	120 °C
RTI Str	1.5mm	UL 746	130 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	147 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	144 °C
Vicat softening temperature		ISO 306/B50	149 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	6E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	130 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:4.00mm	Internal Method	0.40-0.60 %
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.30-0.50 %
Water absorption rate	23°C,24hr	ISO 62	0.16 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	35 KV/mm
Relative permittivity	100Hz	IEC 60250	3.20
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.20
Dissipation factor	100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index		IEC 60112	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.