PC EXL6013-88225 SABIC EU

Form：Granules | Grade：Injection grade

Properties:

High mobilityDuctility at low temperatShort molding cycle

Typical Applications:

Electronic and Electrical ApplicationsAerospace Applicationslens

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic and Electrical Applications \| Aerospace Applications \| lens
Properties:	High mobility \| Ductility at low temperat \| Short molding cycle

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Impact strength of cantilever beam gap	23°C	ISO 180/1A	70	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	60	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	75	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	70	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.00mm	UL 94	V-1
Burning wire flammability index	1.00mm	IEC 60695-2-12	850	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	2100	Mpa
tensile strength	Yield	ISO 527-2/50	55.0	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	60.0	Mpa
Tensile strain	Yield	ISO 527-2/50	7.0	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	100	%
Bending modulus		ISO 178	2150	Mpa
bending strength		ISO 178	80.0	Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	10.0	mg
thermal performance	Test Condition	Test Method	Test Result	Test Unit
1.8MPa, unannealed, 100mm span		ISO 75-2/Ae	122	°C
0.45MPa, unannealed, 100mm span		ISO 75-2/Be	131	°C
thermal conductivity		ISO 8302	0.20	W/m/K
Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	7E-05	cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	5.50	cm3/10min
Shrinkage rate	MD1	Internal Method	0.60-0.80	%
Water absorption rate	Saturation,23°C	ISO 62	0.35	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 3
Dissipation factor	1MHz	IEC 60250	0.010
	Dissipation factor	60Hz	IEC 60250	1E-03
	Dissipation factor	Dissipation factor	50Hz	IEC 60250	1E-03
Relative permittivity	1MHz	IEC 60250	2.70
	Relative permittivity	60Hz	IEC 60250	2.70
	Relative permittivity	Relative permittivity	50Hz	IEC 60250	2.70
Dielectric strength	3.20mm,in Oil	IEC 60243-1	17	KV/mm
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H358/30	ISO 2039-1	90.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.