'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC EXL9112-111 SABIC INNOVATIVE SPAIN
156
Form：Granules | Grade：Light diffusion level
Properties:
High mobilityDuctility at low temperatShort molding cycle
Typical Applications:
Electronic and Electrical ApplicationsPlastic baglensIndustrial applications
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Electronic and Electrical Applications | Plastic bag | lens | Industrial applications |
| Properties: | High mobility | Ductility at low temperat | Short molding cycle |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 25 | kJ/m² |
| 23°C | ISO 179/1eA | 60 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 560 | J/m |
| 23°C | ASTM D256 | 730 | J/m | |
| -30°C8 | ISO 180/1A | 18 | kJ/m² | |
| -30°C9 | ISO 180/1A | 20 | kJ/m² | |
| 23°C9 | ISO 180/1A | 55 | kJ/m² | |
| 23°C8 | ISO 180/1A | 53 | kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak | |
| 23°C | ISO 180/1U | NoBreak | ||
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 67.9 | J |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ISO 4589-2 | 40 | % | |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 825 | °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 | °C |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA | |
| 1.5mm | UL 94 | V-0 | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | ISO 178 | 88.0 | Mpa | |
| Yield,50.0mmSpan | ASTM D790 | 95.1 | Mpa | |
| Bending modulus | ISO 178 | 2300 | Mpa | |
| 50.0mmSpan | ASTM D790 | 2340 | Mpa | |
| Tensile strain | Break | ISO 527-2/50 | 100 | % |
| elongation | Break | ASTM D638 | 100 | % |
| Tensile strain | Yield | ISO 527-2/50 | 5.0 | % |
| elongation | Yield | ASTM D638 | 5.8 | % |
| Tensile modulus | ASTM D638 | 2270 | Mpa | |
| ISO 527-2/1 | 2200 | Mpa | ||
| tensile strength | Yield | ASTM D638 | 58.1 | Mpa |
| Yield | ISO 527-2/50 | 59.0 | Mpa | |
| Break | ASTM D638 | 58.5 | Mpa | |
| Break | ISO 527-2/50 | 55.0 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTM D648 | 136 | °C |
| RTI Str | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 120 | °C | |
| RTI Elec | UL 746 | 130 | °C | |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7.5E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7.2E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 136 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTM D648 | 124 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 124 | °C | |
| Vicat softening temperature | ASTM D152511 | 143 | °C | |
| -- | ISO 306/B50 | 143 | °C | |
| -- | ISO 306/B120 | 144 | °C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.2E-05 | cm/cm/°C |
| MD：23to80°C | ISO 11359-2 | 7.5E-05 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ASTM D792 | 1.18 | g/cm³ | |
| ISO 1183 | 1.19 | g/cm³ | ||
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 17 | g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 16.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.40-0.80 | % |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.15 | % | |
| Outdoor applicability | UL 746C | f1 | ||
| Shrinkage rate | TD：3.20mm | Internal Method | 0.40-0.80 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Compared to the anti leakage trace index | IEC 60112 | PLC 3 | ||
| Dissipation factor | 1MHz | IEC 60250 | 0.010 | |
| 60Hz | IEC 60250 | 4E-04 | ||
| 50Hz | IEC 60250 | 4E-04 | ||
| Relative permittivity | 1MHz | IEC 60250 | 2.70 | |
| 60Hz | IEC 60250 | 2.70 | ||
| 50Hz | IEC 60250 | 2.70 | ||
| Dielectric strength | 3.20mm,in Oil | IEC 60243-1 | 19 | KV/mm |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Ball Pressure Test | H358/30 | ISO 2039-1 | 95.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.