PBT LONGLITE® 1100-211M
45
- Properties:wear resistantHigh temperature resistanUV resistanceHigh viscosityPhysical strength and touThe surface of the formedHigh viscosityPhysical strength and touThe surface of the formed
- Usages:Household appliancesHousehold appliancesProfileAdhesive plasticFastener assemblyComputer keyboardStationery shellKnob switch.
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Fiber Content | Ash | 0 % | |
| density | ASTM D-792 | 1.30-1.32 | |
| Shrinkage rate | ASTM D-955 | 0.8-2.0 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.06 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D-256 | 5.0-6.0 kg.cm/cm | |
| tensile strength | ASTM D-638 | 500-600 kg/cm | |
| elongation at break | ASTM D-638 | 120-180 % | |
| Flexural modulus | ASTM D-790 | 23000 kg/cm | |
| bending strength | ASTM D-790 | 750-850 kg/cm | |
| Rockwell hardness | ASTM D-785 | 85-90 M-scale |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | ASTM D-149 | 20 KV/mm | |
| dielectric constant | ASTM D-150 | 3.3 | |
| Induced positive connection | ASTM D-150 | 0.001 | |
| Volume resistivity | ASTM D-257 | >10 Ω.cm | |
| Surface Resistivity | ASTM D-257 | >10 Ω | |
| arc resistance | ASTM D-495 | 120 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D-696 | 9 10 | |
| Heat distortion temperature | ASTM D-648 | 155 °C | |
| ASTM D-648 | 60 °C | ||
| melting temperature | DSC | 225 °C | |
| flame resistance | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.