PP Homopolymer SH 50 Ducor Petrochemicals BV

Usages:
Loading box
shell
container
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	0.910 g/cm³
melt mass-flow rate		ISO 1133	4.2 g/10min

hardness	Test Condition	Test Method	Test Result
ball-indentation hardness		ISO 2039-1	53.0 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	无断裂
Impact strength of cantilever beam gap		ISO 180/1A	2.0 kJ/m²
	Impact strength of cantilever beam gap		ISO 180/1A	3.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	4.0 kJ/m²
Charpy Notched Impact Strength		ISO 179/1eA	2.5 kJ/m²
Impact strength of cantilever beam gap		ISO 180/1A	11 kJ/m²
Charpy Notched Impact Strength		ISO 179/1eA	4.0 kJ/m²
	Charpy Notched Impact Strength		ISO 179/1eA	5.5 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	11 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	70 kJ/m²
	Impact strength of simply supported beam without notch		ISO 179/1eU	80 kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	140 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	1200 MPa
tensile strength	Yield	ISO 527-2/50	27.0 MPa
Tensile strain	Yield	ISO 527-2/50	7.0 %
Tensile strain	Tensile strain	Break	ISO 527-2/50	>50 %
Tensile creep modulus		ISO 899-1	260 MPa
shear modulus		ISO 6721-2	590 MPa

Thermal performance	Test Condition	Test Method	Test Result
vicat		ISO 306/A	150 °C
vicat	vicat		ISO 306/B	71.0 °C
melting temperature		ISO 3146	163 °C
Heat distortion temperature		ISO 75-2/B	75.0 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	54.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.