Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.35 g/cm³ |
| Water absorption rate | | ISO 62 | 6.7 % |
| Water absorption rate | | ISO 62 | 2.3 % |
| viscosity number | | ISO 307 | 150 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 220 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 45 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 6400 MPa |
| tensile strength | Yield | ISO 527-2/50 | 110 MPa |
| tensile strength | Break | ISO 527-2/5 | 110 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 2.7 % |
| Tensile strain | Break | ISO 527-2/5 | 2.7 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Surface Resistivity | | IEC 60093 | 1E+10 ohms |
| Volume resistivity | | IEC 60093 | 1E+12 ohms·cm |
| relative permittivity | | IEC 60250 | 3.90 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 215 °C |
| Heat distortion temperature | | ISO 75-2/A | 200 °C |
| melting temperature | | ISO 11357-3 | 220 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.0E-5到1.1E-4 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 3.4E-5到3.8E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare