'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC/ABS 6140 SABIC INNOVATIVE NANSHA
115
Form：Granules | Grade：Injection grade
Properties:
Flame retardantHigh impact resistance
Typical Applications:
Automotive interior partsElectrical applications
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive interior parts | Electrical applications |
| Properties: | Flame retardant | High impact resistance |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 50.0 | J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 | kJ/m² |
| 23°C | ISO 179/1eA | 10 | kJ/m² | |
| -30°C | ASTM D256 | 88 | J/m | |
| 23°C | ASTM D256 | 200 | J/m | |
| -30°C | ISO 180/1A | 5.0 | kJ/m² | |
| 23°C | ISO 180/1A | 10 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.600mm | UL 94 | V-1 | |
| 0.800mm | UL 94 | V-0 | ||
| 1.50mm | UL 94 | 5VB | ||
| Burning wire flammability index | 0.800mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.00mm | IEC 60695-2-13 | 850 | °C |
| 3.00mm | IEC 60695-2-13 | 800 | °C | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| --1 | ASTM D638 | 3500 | Mpa | |
| yield | ASTM D638 | 65.0 | Mpa | |
| ASTM D638 | 65.0 | Mpa | ||
| crack | ASTM D638 | 50.0 | Mpa | |
| ISO 527-2/5 | 50.0 | Mpa | ||
| yield | ASTM D638 | 4.0 | % | |
| ISO 527-2/5 | 3.5 | % | ||
| crack | ASTM D638 | 100 | % | |
| ISO 527-2/50 | 15 | % | ||
| 50.0mm span | ASTM D790 | 3300 | Mpa | |
| --8 | ISO 178 | 3450 | Mpa | |
| --9 | ISO 178 | 97.0 | Mpa | |
| Yield, 50.0mm span | ASTM D790 | 100 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| 0.45MPa, unannealed, 6.40mm | ASTM D648 | 97.0 | °C | |
| 1.8MPa, unannealed, 3.20mm | ASTM D648 | 83.0 | °C | |
| 1.8MPa, unannealed, 6.40mm | ASTM D648 | 89.0 | °C | |
| 1.8MPa, unannealed, 64.0mm span of | ISO 75-2/Af | 80.0 | °C | |
| Ball Pressure Test | 75°C | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 5.5E-05 | cm/cm/°C |
| TD:-40to40°C | ASTME831 | 6E-05 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 18 | g/10min |
| Melt Volume Flow Rate (MVR) | 220°C/5.0kg | ISO 1133 | 14.0 | cm3/10min |
| Shrinkage rate | MD:3.20mm | Internal Method | 0.30-0.50 | % |
| TD:3.20mm | Internal Method | 0.40-0.60 | % | |
| 24hr,50%RH | ASTM D570 | 0.010 | % | |
| 24hr | ASTM D570 | 0.10 | % | |
| Saturation, 23 ° C | ISO 62 | 0.090 | % | |
| Balance, 23 ° C, 50% RH | ISO 62 | 0.010 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | ASTM D257 | 3.5E+15 | ohms | |
| Volume resistivity | ASTM D257 | 2.7E+16 | ohms·cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.