PBI (T Series) TF-60C PBI USA

Properties:
Fillers
carbon fiber reinforced materials
Usages:
Semiconductor molded compounds
gears
electrical
electronic applications
business equipment
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density			1.41 g/cm³
Water absorption rate		ASTM D570	0.15 %
Water absorption rate	Water absorption rate	Equilibrium	ASTM D570	4.0 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	30

Supplementary Information	Test Condition	Test Method	Test Result
Initial weightlessness temperature		内部方法	599 °C
Initial weightlessness temperature	Initial weightlessness temperature		内部方法	627 °C

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	24100 MPa
tensile strength		ASTM D638	228 MPa
elongation	Break	ASTM D638	1.4 %
Flexural modulus		ASTM D790	21000 MPa
bending strength		ASTM D790	321 MPa
Compression Modulus		ASTM D695	3790 MPa
compressive strength		ASTM D695	221 MPa
Poisson's ratio			0.39

Thermal performance	Test Method	Test Result
Heat distortion temperature	ASTM D648	320 °C
Linear coefficient of thermal expansion	TMA	2.6E-05 cm/cm/°C
thermal conductivity	ASTMF433	0.45 W/m/K
HeatCapacity	DSC	1170 J/kg/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.