Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.35 -- |
| Shrinkage rate | | % | 0.30to0.40 -- |
| Water absorption rate | | % | 0.95 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 122 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | MPa | 240 140 |
| Tensile modulus | | MPa | 8000 5000 |
| tensile strength | | MPa | 150 100 |
| elongation | Break | % | 3.0 4.5 |
| Flexural modulus | | MPa | 8000 4500 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 120 180 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 22 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 210 -- |
| Heat distortion temperature | | °C | 200 -- |
| Continuous use temperature | | °C | 100to110 -- |
| melting temperature | | °C | 214to220 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 2.5E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.