Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.16 g/cm³ |
| Shrinkage rate | | 内部方法 | 1.2 % |
| Water absorption rate | | ASTMD570 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTMD2863 | >30 % |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTMD638 | 80.0 MPa |
| elongation | Break | ASTMD638 | 25 % |
| Flexural modulus | | ASTMD790 | 3200 MPa |
| bending strength | | ISO 178 | 95.0 MPa |
| bending strength | Break | ASTM D790 | 95.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 3.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| dielectric strength | | ASTMD149 | 37 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 1218 | 218 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.5E-05 cm/cm/°C |
| Heat distortion temperature | | ASTMD648 | 200 °C |
| Heat distortion temperature | | ASTMD648 | 75.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.