Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.15 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.10to0.20 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2600 MPa |
| tensile strength | Yield | ISO 527-2 | 60.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 5.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 47 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | >1.0E+14 ohms |
| Volume resistivity | | ASTM D257 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/A | 128 °C |
| vicat | | ISO 306/B | 116 °C |
| Heat distortion temperature | | ISO 75-2/B | 119 °C |
| Heat distortion temperature | | ISO 75-2/A | 102 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare