ABS 100 TORAY MALAYSIA

Form：Granules | Grade：Injection grade

Properties:

High impact resistance

Typical Applications:

Industrial machineryFitness equipment

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative Model(2)

Product Description

Typical Applications:	Industrial machinery \| Fitness equipment
Properties:	High impact resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	310	J/m
	Impact strength of cantilever beam gap	23°C,12.7mm	ASTM D256	290	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	0°C,12.7mm	ASTM D256	200	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	26	kJ/m²
Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	160	J/m
	Impact strength of cantilever beam gap	-30°C,12.7mm	ASTM D256	140	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	0°C,3.20mm	ASTM D256	230	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	63.0	Mpa
Tensile modulus		ISO 527-2/1	2100	Mpa
tensile strength	Yield	ASTM D638	41.0	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	44.0	Mpa
elongation	Break	ASTM D638	40	%
Tensile strain	Break	ISO 527-2/50	>10	%
Bending modulus		ASTM D790	1960	Mpa
bending strength		ASTM D790	63.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	85.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	91.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0	°C
Linear coefficient of thermal expansion	MD	ASTM D696	7.6E-05	cm/cm/°C
thermal conductivity		ASTMC177	0.15	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.04	g/cm³
density	density		ISO 1183	1.04	g/cm³
melt mass-flow rate	220°C/10.0kg	ISO 1133	15	g/10min
Shrinkage rate	MD	ASTM D955	0.40-0.60	%
Water absorption rate	23°C,24hr	ASTM D570	0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	>1.0E+16	ohms
Volume resistivity	23°C	ASTM D257	>1.0E+16	ohms·cm
Dielectric strength		ASTM D149	24	KV/mm
Dielectric constant	1kHz	ASTM D150	3.10
Dissipation factor	1kHz	ASTM D150	6.5E-03
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	105

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.