GPPS TAIRIREX® GP550N FORMOSA NINGBO
23
- Properties:currencyhigh molecular weight
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.04 | g/cm³ | |
| 23°C | ISO1183 | 1.04 | g/cm³ | |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 2.3 | g/10min |
| 200°C/5.0kg | ISO1133 | 2.3 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23°C | ASTMD638 | 51.0 | Mpa |
| 屈服,23°C | ISO527-2 | 51.0 | Mpa | |
| elongation | 断裂,23°C | ASTMD638 | 2.0 | % |
| 断裂,23°C | ISO527-2 | 2.0 | % | |
| Bending modulus | 23°C | ASTMD790 | 3330 | Mpa |
| 23°C | ISO178 | 3330 | Mpa | |
| bending strength | 23°C | ASTMD790 | 98.1 | Mpa |
| 23°C | ISO178 | 98.0 | Mpa | |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ISO180 | 18 | J/m |
| 23°C,6.35mm | ASTMD256 | 18 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Annealed,3.18mm | ASTMD648 | 95.0 | °C |
| 1.8MPa,Annealed,3.18mm | ISO75-2/A | 95.0 | °C | |
| vicat softening point | ASTMD1525 | 104 | °C | |
| ISO306/B | 104 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm,NC | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Residual Monomer | <700 | ppm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.