PC 3413R-131 COVESTRO GERMANY

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedenhanceFlame retardant

Typical Applications:

Automotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector
Properties:	Glass fiber reinforced \| enhance \| Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C	ASTM D3029	5.00	J
Impact strength of cantilever beam gap		ASTM D1822	67.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-1
	UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield,50.0mmSpan	ASTM D790	153	Mpa
Bending modulus	50.0mmSpan	ASTM D790	6610	Mpa
elongation	Break	ASTM D638	2.0	%
tensile strength	Break	ASTM D638	100	Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	24.0	mg
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec		UL 746	120	°C
RTI Imp		UL 746	120	°C
RTI Str		UL 746	130	°C
thermal conductivity		ASTMC177	0.22	W/m/K
specific heat		ASTMC351	1130	J/kg/°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	151	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	146	°C
Vicat softening temperature		ASTM D15255	165	°C
Linear coefficient of thermal expansion	MD：-40to95°C	ASTME831	2.2E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C	ASTM D570	0.26	%
Water absorption rate	Water absorption rate	24hr	ASTM D570	0.14	%
Shrinkage rate	MD：3.20mm	Internal Method	0.10-0.30	%
melt mass-flow rate	300°C/5.0kg	ASTM D1238	19	g/10min
melt mass-flow rate	melt mass-flow rate	300°C/1.2kg	ASTM D1238	5.0	g/10min
Specific volume		ASTM D792	0.697	cm³/g
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	>1.0E+17	ohms·cm
Dielectric strength	3.20mm,inAir	ASTM D149	19	KV/mm
Dielectric constant	50Hz	ASTM D150	3.35
Dielectric constant	Dielectric constant	60Hz	ASTM D150	3.35
Hot wire ignition	HWI	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 3
High arc combustion index	HAI	UL 746	PLC 4
Compared to the anti leakage trace index	CTI	UL 746	PLC 5
Arc resistance		ASTM D495	PLC7
Dissipation factor	1MHz	ASTM D150	7E-03
	Dissipation factor	60Hz	ASTM D150	1.1E-03
	Dissipation factor	Dissipation factor	50Hz	ASTM D150	1.1E-03
Dielectric constant	1MHz	ASTM D150	3.31
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ASTM D785	92
Rockwell hardness	Rockwell hardness	R-Sale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.