EPDM S552-1 SK KOREA

196

Form：Granules | Grade：Withdrawal level

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	36	%
Acid gas release		IEC 60754-2	4.00	µS/cm
Acid gas release	Acid gas release	pH	IEC 60754-2	5.70
Combustion temperature index		ISO 4589-3	280	°C
smoke density	Flamingmode	ASTME662	<60	Ds
smoke density	smoke density	Non-flamingmode	ASTME662	<140	Ds
toxicity		NES713	0.600
elastomer	Test Condition	Test Method	Test Result	Test Unit
tear strength		BS646999.1	8.00	kN/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	after7days,inIRM903Oil:23°C		12.5	Mpa
	tensile strength	after7days,inIRM902Oil:23°C		14.5	Mpa
		tensile strength	after4hours,inSAE20Oil:70°C		13.5	Mpa
		tensile strength	tensile strength	after4hours,inIRM902Oil:70°C		13.5	Mpa
Elongation at Break	after7days,inIRM903Oil:23°C		160	%
	Elongation at Break	after7days,inIRM902Oil:23°C		220	%
		Elongation at Break	after4hours,inSAE20Oil:70°C		180	%
		Elongation at Break	Elongation at Break	after4hours,inIRM902Oil:70°C		210	%
tensile strength	--2	IEC 60811-1-2	15.0	Mpa
	tensile strength	--3	IEC 60811-1-2	17.0	Mpa
	tensile strength	tensile strength	--	IEC 60811-1-1	14.0	Mpa
Tensile strain	Break2	IEC 60811-1-2	170	%
	Tensile strain	Break3	IEC 60811-1-2	170	%
	Tensile strain	Tensile strain	Break	IEC 60811-1-1	200	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot pressing test	90°C	IEC 60811-3-1	35	%
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	150°C/21.6kg	ISO 1133	5.5	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD	ASTM D2240	59
aging	Test Condition	Test Method	Test Result	Test Unit
Tensile stress change rate	70°C,168hr,inWater，Break	BS646999.1	-5.0	%
	Tensile stress change rate	70°C,4hr,inSAE20Oil，Break		-10	%
		Tensile stress change rate	70°C,4hr,inIRM902Oil，Break		5.0	%
			Tensile stress change rate	23°C,168hr,inIRM903Oil，Break		-20	%
			Tensile stress change rate	Tensile stress change rate	23°C,168hr,inIRM902Oil，Break		10	%
Change rate of tensile strength in air	70°C,168hr,inWater	BS646999.1	-12	%
	Change rate of tensile strength in air	70°C,4hr,inSAE20Oil		-5.0	%
		Change rate of tensile strength in air	70°C,4hr,inIRM902Oil		-5.0	%
			Change rate of tensile strength in air	23°C,168hr,inIRM903Oil		-10	%
			Change rate of tensile strength in air	Change rate of tensile strength in air	23°C,168hr,inIRM902Oil		5.0	%
Tensile stress change rate	110°C,168hr，Break		-15	%
Tensile stress change rate	Tensile stress change rate	100°C,168hr，Break		-15	%
Change rate of tensile strength in air	110°C,168hr		20	%
Change rate of tensile strength in air	Change rate of tensile strength in air	100°C,168hr		5.0	%
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
HalogenAcidGasEvolution		IEC 60754-1	0.0	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

EPDM S552-1 SK KOREA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index