PCTG TX1001(箱装) EASTMAN USA

Form：Granules

Properties:

heat-resistingHydrolysis resistanceHigh impact resistanceProcessabilitytransparentChemical resistance

Typical Applications:

Electrical fieldElectronic fieldHousehold appliancesHousehold appliancesHousehold goodsFood service sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Household appliances \| Household appliances \| Household goods \| Food service sector
Properties:	heat-resisting \| Hydrolysis resistance \| High impact resistance \| Processability \| transparent \| Chemical resistance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	Total	ASTM D1003	90.0	%
turbidity		ASTM D1003	<1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ASTM D4812	NoBreak
	Impact strength of cantilever beam gap	23°C	ASTM D256	980	J/m
		Impact strength of cantilever beam gap	-40°C	ISO 180	20	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	93	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ASTM D638	1550	Mpa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	1550	Mpa
tensile strength	Yield,23°C	ASTM D638	43.0	Mpa
	tensile strength	Yield,23°C	ISO 527-2	43.0	Mpa
		tensile strength	Break,23°C	ASTM D638	53.0	Mpa
		tensile strength	tensile strength	Break,23°C	ISO 527-2	58.0	Mpa
elongation	Yield,23°C	ASTM D638	6.0	%
Tensile strain	Yield,23°C	ISO 527-2	7.0	%
elongation	Break,23°C	ASTM D638	210	%
Tensile strain	Break,23°C	ISO 527-2	190	%
Bending modulus	23°C	ASTM D790	1550	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	1500	Mpa
bending strength	23°C	ISO 178	59.0	Mpa
bending strength	bending strength	Yield,23°C	ASTM D790	62.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	99.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.18	g/cm³
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.