Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Resistance to environmental stress cracking | | ISO16770 | 400 hr |
| Melt flow ratio | | | 25.0到31.0 |
| density | | ISO1183 | 0.947到0.951 g/cm³ |
| melt mass-flow rate | | ISO1133 | 5.2到7.2 g/10min |
| melt mass-flow rate | | ISO1133 | 0.20到0.26 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 62 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ResistancetoInternalPressure-HydrostaticStrength | | ISO1167 | >2 yr |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2/50 | 23.0 MPa |
| Tensile stress | Break | ISO527-2/50 | 36.0 MPa |
| Tensile strain | Yield | ISO527-2/50 | 10 % |
| Tensile strain | Break | ISO527-2/50 | >1000 % |
| Tensile strain | | ISO527-2/50 | 850 MPa |
| ResistancetoSlowCrackGrowth-NotchTest | | ISO13479 | >1000 hr |
| Resistant to rapid crack propagation, Pc-TestS | | ISO13477 | >20.0 bar |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 25 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTMD746 | <-80.0 °C |
| vicat | | ISO306/B50 | 74.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.