Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.34 -- |
| Water absorption rate | | % | 6.6 -- |
| Water absorption rate | | % | 2.3 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 122 112 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| UL flame retardant rating | | | HB -- |
| Hot filament ignition temperature | | °C | 650 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | MPa | 170 110 |
| elongation | Break | % | 3.5 4.0 |
| Flexural modulus | | MPa | 8000 4500 |
| bending strength | | MPa | 250 150 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | J/m | 100 130 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 1E+11 |
| dielectric strength | | kV/mm | 60 40 |
| dielectric constant | | | 3.80 -- |
| Dissipation Factor | | | 0.025 -- |
| Surface Resistivity | | ohms | 1E+12 1E+10 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 215 -- |
| Heat distortion temperature | | °C | 210 -- |
| melting temperature | | °C | 215to220 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 2.3E-05 -- |
| thermal conductivity | | W/m/K | 0.28 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.