PA12 Grilamid® L 25 W 40 HL X EMS-GRIVORY

Usages:
Hydraulic applications automotive applications industrial applications consumer goods applications pneumatic applications
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C		无断裂
Charpy Notched Impact Strength	-30°C	kJ/m²	10 --
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C		无断裂 --
Impact strength of simply supported beam without notch	-30°C		无断裂

flammability	Test Condition	Test Method	Test Result
Flammability level	0.8mm		HB --

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break	%	>50 --
Nominal tensile fracture strain		%	>50 --
Tensile modulus		MPa	380 360
tensile strength	Yield	MPa	25.0 --
tensile strength	tensile strength	Break	MPa	40.0 40.0
Tensile strain	Yield	%	20 --

thermal performance	Test Condition	Test Method	Test Result
Continuous use temperature	--2	°C	80.0to110 --
Continuous use temperature	Continuous use temperature	--3	°C	150 --
Melting temperature		°C	173 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	1.4E-04 --
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	cm/cm/°C	1.8E-04 --
Hot deformation temperature	0.45MPa,Unannealed	°C	95.0 --
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	°C	45.0 --

Physical properties	Test Condition	Test Method	Test Result
density		g/cm³	1.02 --
Water absorption rate	Equilibrium,23°C,50%RH	%	0.70 --
Shrinkage rate	TD	%	1.2 --
Shrinkage rate	Shrinkage rate	MD	%	0.90 --
Water absorption rate	Saturation,23°C	%	1.4 --

Electrical performance	Test Method	Test Result
Surface resistivity	ohms	-- 1E+12
Volume resistivity	ohms·cm	-- 1E+13
Dielectric strength	kV/mm	32 --
Compared to the anti leakage trace index	V	--

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD,15Sec		63 --

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.