Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.05 g/cm³ |
| Apparent density | | | 0.60 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 30 g/10min |
| Shrinkage rate | | | 0.40to0.70 % |
| Water absorption rate | | ISO 62 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 70 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3100 MPa |
| tensile strength | Break | ISO 527-2 | 35.0 MPa |
| Tensile strain | Break | ISO 527-2 | 2.0 % |
| Flexural modulus | | ISO 178 | 2900 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| dielectric strength | | | 140 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | | 7.1E-05 cm/cm/°C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 84.0 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 96.0 °C |
| vicat | | ISO 306/A50 | 105 °C |
| vicat | | ISO 306/B50 | 101 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.