Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.19 g/cm³ |
| melt mass-flow rate | | ISO1133 | 10 g/10min |
| Melt volume flow rate | | ISO1133 | 10.0 cm³/10min |
| Shrinkage rate | | ISO294-4 | 2.1 % |
| Shrinkage rate | | ISO294-4 | 2.2 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 52 |
| | ISO868 | 58 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO3795 | 42 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Odor | | VDA270 | 3.50 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 190 MPa |
| Tensile stress | Break | ISO527-2 | 35.0 MPa |
| Tensile stress | | ISO527-2 | 7.80 MPa |
| Tensile stress | | ISO527-2 | 11.9 MPa |
| Tensile stress | | ISO527-2 | 19.0 MPa |
| Tensile strain | Break | ISO527-2 | >300 % |
| Nominal tensile fracture strain | | ISO527-2 | 380 % |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Melt density | | | 1.01 g/cm³ |
| SpecificHeatCapacity of Melt | | | 2150 J/kg/°C |
| ThermalConductivityofMelt | | | 0.16 W/m/K |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 20 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 39 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Tensile impact strength | | ISO8256/1 | 330 kJ/m² |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| | ISO34-1 | 140 kN/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ISO974 | -54.0 °C |
| melting temperature | | ISO11357-3 | 211 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.