PVDF 720 ARKEMA CHANGSHU

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative(1)

Product Description

Certificates

Technical Data Sheet

UL	Test Condition	Test Method	Test Result	Test Unit
RTI Str	本色 1.5mm	UL 746B	150	°C
Outdoor applicability		UL -746C	f1
UL flame retardant rating	1.5mm	UL 94	V-0
RTI Elec	本色 1.5mm	UL 746B	150	°C
RTI Imp	本色 1.5mm	UL 746B	150	°C
optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index	钠光谱D线	ASTM D542	1.42
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23℃	ISO 179	8	kJ/㎡
Suspended wall beam without notch impact strength	23℃	ASTM D256	1.07-4.27	KJ/m
Impact strength of cantilever beam gap	23℃	ASTM D256	0.0801-0.214	KJ/m
Bending modulus	23℃	ASTM D790	1380-2310	Mpa
bending strength	23℃5.0%Strain	ASTM D790	58.6-75.8	Mpa
elongation	Break23℃	ASTM D638	20-100	%
	elongation	Break	ISO 527	50	%
		elongation	Yield23℃	ASTM D638	570	%
		elongation	elongation	Yield	ISO 527	8	%
tensile strength	Break23℃	ASTM D638	34.5-55.2	Mpa
	tensile strength	Yield23℃	ASTM D638	44.8-55.2	Mpa
	tensile strength	tensile strength	Yield	ISO 527	54	Mpa
Tensile modulus	23℃	ASTM D638	1380-2310	Mpa
Tensile modulus	Tensile modulus		ISO 527	2200	Mpa
Charpy Notched Impact Strength	-30°C	ISO 179	5	kJ/㎡
	Charpy Notched Impact Strength	23℃	ISO 179	208	kJ/㎡
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃	ISO 179	189	kJ/㎡
Friction coefficient	静态对钢23℃	ASTM D1894	0.2
Friction coefficient	Friction coefficient	静态对钢23℃	ASTM D1894	0.14
Taber wear resistance	CS-17轮1kg	ASTM G195	5-9	mg/1000cy
Compression slip	23℃	ASTM D695	68.9-103	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa	ISO 75	110	°C
	Hot deformation temperature	1.8MPa120℃/hr	ASTM D648	105-115	°C
		Hot deformation temperature	0.45MPa	ISO 75	132	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa120℃/hr	ASTM D648	125-140	°C
Vicat softening temperature	50℃/hr 50N	ISO 306	139	°C
Melting temperature	10℃/min	ISO 11357	168	°C
Melting temperature	Melting temperature		ASTM D3418	165-172	°C
Glass transition temperature	10℃/min	ISO 11357	-40	°C
Glass transition temperature	Glass transition temperature		ASTM D7028	-40.6-38.3	°C
Linear coefficient of thermal expansion	Flow	ISO 11359	0.00015	m/m/k
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	23℃	ASTM D696	1.19E-3	cm/cm/℃
thermal conductivity		ASTM E1461	0.17-0.19	W/(m.K)
specific heat		内部测试方法	745-958	J/(kg.k)
decomposition temperature	TGA在空气中1 %质量损失	内部测试方法	375	°C
decomposition temperature	decomposition temperature	TGA在通气中1%质量损失	内部测试方法	410	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	230℃100s	ASTM D3835	6-12	kPoise
melt mass-flow rate	230°C 3.8kg	ASTM D1238	5-26.5	g/10min
Yirong Index	230℃ 5kg	ISO 1133	10	㎤/10min
Water absorption rate		ISO 62	0.015	%
	Water absorption rate		ASTM D570	0.01-0.03	%
	Water absorption rate	Water absorption rate		ISO 62	0.03	%
Shrinkage rate	垂直	ISO 294	2	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294	2	%
density	23℃	ASTM D792	1.77-1.79	g/㎤
density	density		ISO 1183	1780	kg/㎥
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1000000000000000	Ω
Accumulation resistor		IEC 60093	2000000000000	Ω.m
Volume resistivity	20℃ 65RH	ASTM D257	200000000000000	Ω.cm
Dielectric strength		IEC 60243	21	KV/mm
Dielectric strength	Dielectric strength	23℃	ASTM D149	1.7	KV/mm
Dielectric constant	100Hz	IEC 60250	9
	Dielectric constant	1MHz	IEC 60250	7
	Dielectric constant	Dielectric constant	iKHz	ASTM D150	4.5-9.5
Dissipation factor	100Hz	IEC 60250	0.032
	Dissipation factor	1MHz	IEC 60250	0.214
	Dissipation factor	Dissipation factor	100kHz	ASTM D150	0.01-0.21
Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	23℃	ASTM D2240	76-80
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
Extreme Oxygen Index		ISO 4589	43	%
Extreme Oxygen Index	Extreme Oxygen Index		ASTM D2863	44	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.