Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.52 g/cm³ |
| Apparent density | | ISO 60 | 0.78 g/cm³ |
| Shrinkage rate | | ISO 2577 | 0.60 % |
| Water absorption rate | | ISO 62 | 20.0 mg |
| Shrinkage rate | | ISO 2577 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 350 MPa |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Compression molding pressure | | | >15.0 MPa |
| Compression molding temperature | | | 160to190 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 8000 MPa |
| bending strength | | ISO 178 | 90.0 MPa |
| compression stress | | ISO 604 | 250 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 1.8 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+10 ohms |
| Volume resistivity | | IEC 60093 | 1E+11 ohms·cm |
| dielectric strength | | IEC 60243-1 | 5.0 kV/mm |
| Dissipation Factor | | IEC 60250 | 0.20 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/C | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.