ABS 3100 TAIDA TAIWAN

121

Form：Granules | Grade：Heat resistant grade

Properties:

Ultra high impact resistaWidely used for extrusionUltra high impact strengtGood processabilityExcellent hot forming

Typical Applications:

Used for luggageToolboxLocomotive partsLow temperature productsHelmetBus boxheelControlled pipe fittings etcApplication in the automotive fieldFootwear

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative(1)

Product Description

Typical Applications:	Used for luggage \| Toolbox \| Locomotive parts \| Low temperature products \| Helmet \| Bus box \| heel \| Controlled pipe fittings \| etc \| Application in the automotive field \| Footwear
Properties:	Ultra high impact resista \| Widely used for extrusion \| Ultra high impact strengt \| Good processability \| Excellent hot forming

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	450	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	490	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D-570	0.3	wt%
density		ASTM D-792	1.03
melt mass-flow rate	200℃/5kg	ASTM D-1238	8.0	g/10min
melt mass-flow rate	melt mass-flow rate	200℃/5kg	ASTM D-1238	0.8	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23℃ 2.8mm/min	ASTM D-790	8500	psi
bending strength	bending strength	23℃ 2.8mm/min	ASTM D-790	600	kg/cm
Elongation at Break	1/8"	ASTM D-638	50	%
tensile strength	1/8"，Break	ASTM D-638	300	psi
	tensile strength	1/8"，Break	ASTM D-638	4300	kg/cm
		tensile strength	23℃，Yield	ASTM D-638	5000	psi
		tensile strength	tensile strength	23℃，Yield	ASTM D-638	350	kg/cm
Impact strength of cantilever beam gap	23℃1/8"	ASTM D-256	53 (9.8)	kg.cm/cm(ft.1b/in)
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃1/2"	ASTM D-256	38 (7.0)	kg.cm/cm(ft.1b/in)
Rockwell hardness			100
flexural coefficient	23℃ 2.8mm/min	ASTM D-790	290000	psi
flexural coefficient	flexural coefficient	23℃ 2.8mm/min	ASTM D-790	20000	kg/cm
bending strength	Yield,23°C	ASTM D790	58.6	Mpa
Bending modulus	23°C	ASTM D790	2000	Mpa
elongation	Break,23°C,3.18mm	ASTM D638	90	%
tensile strength	Break,23°C,3.18mm	ASTM D638	27.6	Mpa
tensile strength	tensile strength	Yield,23°C,3.18mm	ASTM D638	32.4	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D15254	102	°C
UL flame retardant rating		UL 94	HB
Vicat softening temperature		ASTM D-1525	100	°C
Hot deformation temperature	Unannealed	ASTM D-1525	85(185)	℃(F)
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ASTM D955	<0.40	%
melt mass-flow rate	220°C/10.0kg	ASTM D1238	8.0	g/10min
melt mass-flow rate	melt mass-flow rate	200°C/5.0kg	ASTM D1238	0.80	g/10min
Shrinkage rate		ASTM D-955	0.4	%
density		ASTM D792	1.03	g/cm³
Water absorption rate	24hr	ASTM D570	<0.30	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.