PC/ABS MB8700 MITSUBISHI THAILAND

Form：Granules | Grade：Flame retardant grade

Properties:

heat-resistingHigh impact resistance

Typical Applications:

ShellElectronic and Electrical Applications

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Shell \| Electronic and Electrical Applications
Properties:	heat-resisting \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.2mm	UL 94	5VB
UL flame retardant rating	UL flame retardant rating	1.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	99.0	Mpa
Bending modulus		ISO 178	3100	Mpa
Nominal tensile fracture strain		ISO 527-2	16	%
Tensile strain	Yield	ISO 527-2	3.5	%
tensile strength	Yield	ISO 527-2	63.0	Mpa
Tensile modulus		ISO 527-2	3100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	81.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	89.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C	ISO 62	0.20	%
Shrinkage rate	MD:3.20mm		0.25-0.45	%
Shrinkage rate	Shrinkage rate	TD:3.20mm		0.25-0.45	%
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	35.0	cm3/10min
melt mass-flow rate	260°C/2.16kg	ISO 1133	35	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.