ABS HH-106 BK10009 INEOS STYRO THAILAND

Form：Granules | Grade：Heat resistant grade

Properties:

heat-resisting

Typical Applications:

Electronic fieldAutomotive sectorAutomotive interior partsApplication in the automotive field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic field \| Automotive sector \| Automotive interior parts \| Application in the automotive field
Properties:	heat-resisting

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	190	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	100	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	102	Mpa
Vicat softening temperature		ISO 306	103	°C
Rockwell hardness			110	R
Bending modulus		ISO 178	24000	kg/cm
bending strength		ISO 178	770	kg/cm
Tensile modulus		ISO 527-2	25000	kg/cm
elongation	Break	ISO 527-2	25	%
elongation	elongation	Yield	ISO 527-2	3.0	%
tensile strength	Break	ISO 527-2	390	kg/cm
tensile strength	tensile strength	Yield	ISO 527-2	520	kg/cm
Tensile modulus		ASTM D638	2500	Mpa
Tensile modulus	Tensile modulus		ISO 527-2	2400	Mpa
tensile strength	Yield,23°C	ASTM D638	52.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	51.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.0	%
elongation	Break	ASTM D638	3.0	%
Nominal tensile fracture strain	23°C	ISO 527-2	9.0	%
Bending modulus		ASTM D790	2400	Mpa
Bending modulus	Bending modulus		ISO 178	2400	Mpa
bending strength		ASTM D790	77.2	Mpa
bending strength	bending strength		ISO 178	72.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B50	106	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	115	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	99.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	107	°C
Maximum operating temperature			85	°C
thermal conductivity		DIN 52612	0.17	W/m/K
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0kg	ASTM D1238	7.0	g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	7.00	cm3/10min
Water absorption rate		ASTM D570	0.3	%
Shrinkage rate	MD	ASTM D955	0.55	%
Shrinkage rate	Shrinkage rate		ISO 294-4	0.40-0.70	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.25	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112		V
Dielectric strength	1.50mm	IEC 60243-1	39	KV/mm
Volume resistivity		IEC 60093	1E+15	ohms·cm
Volume resistivity	Volume resistivity		ASTM D257	>1.0E+15	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.