Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 0.900 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.4 g/10min |
| density | | ASTM D1505 | 0.900 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.4 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 64 |
| Rockwell hardness | R-Scale | ASTM D785 | 64 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Fluidity-HPC | | | 940 mm |
| Fluidity-HPC | | | 940 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 450 % |
| Flexural modulus | | ASTM D790 | 1150 MPa |
| Flexural modulus | | ASTM D790 | 1150 MPa |
| tensile strength | Yield | ASTM D638 | 27.0 MPa |
| tensile strength | Yield | ASTM D638 | 27.0 MPa |
| elongation | Break | ASTM D638 | 450 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 29 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | >500 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | >500 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 29 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525 | 135 °C |
| Heat distortion temperature | | ASTM D648 | 110 °C |
| vicat | | ASTM D1525 | 135 °C |
| Heat distortion temperature | | ASTM D648 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.