Technical Data Sheet

elastomer	Test Condition	Test Method	Test Result	Test Unit
Permanent compression deformation	100°C,22hr	ASTM D395B	95	%
	Permanent compression deformation	24°C,22hr	ISO 815	21	%
	Permanent compression deformation	Permanent compression deformation	70°C,22hr	ISO 815	82	%
Stretch permanent deformation	100%Strain	ASTM D412	5	%
tensile strength	100%Strain	ASTM D412	2.76	MPa
	tensile strength	100%Strain,23°C	ISO 37	2.76	MPa
		tensile strength	Yield,23°C	ASTM D412	9.24	MPa
		tensile strength	tensile strength	Yield,23°C	ISO 37	9.24	MPa
elongation	Break	ASTM D412	420	%
elongation	elongation	Break,23°C	ISO 37	420	%
tear strength	24°C	ASTM D624	37.0	kN/m
Permanent compression deformation	24°C,22hr	ASTM D395B	21	%
	Permanent compression deformation	70°C,22hr	ASTM D395B	82	%
	Permanent compression deformation	Permanent compression deformation	100°C,22hr	ISO 815	95	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber wear resistance	1000Cycles,1.0E+6g,CS-17Wheel	ASTM D1044	87.0	mg
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Brittle temperature		ASTM D746	-67.8	°C
Brittle temperature	Brittle temperature		ISO 812	-67.8	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
MeltViscosity	190°C,300sec^-1	ASTM D3835	420	Pa·s
density		ASTM D792	1.10	g/cm³
density	density		ISO 1183	1.10	g/cm³
Shrinkage rate	MD：1.59mm	ASTM D955	0.90	%
	Shrinkage rate	MD：3.18mm	ASTM D955	1.3	%
		Shrinkage rate	TD：1.59mm	ASTM D955	0.0	%
			Shrinkage rate	TD：3.18mm	ASTM D955	0.40	%
				Shrinkage rate	TD:1.59mm	ISO 294-4	0.0	%
					Shrinkage rate	MD:1.59mm	ISO 294-4	0.90	%
						Shrinkage rate	TD:3.18mm	ISO 294-4	0.40	%
						Shrinkage rate	Shrinkage rate	MD:3.18mm	ISO 294-4	1.3	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreA,5Sec	ASTM D2240	65
Shore hardness	Shore hardness	ShoreA,5Sec	ISO 868	65
aging	Test Condition	Test Method	Test Result	Test Unit
Volume change	24°C,168hr,inReferenceFuelB	ASTM D471	49	%
	Volume change	70°C,168hr,inASTM#1Oil	ASTM D471	5.0	%
		Volume change	70°C,168hr,inIRM903Oil	ASTM D471	42	%
			Volume change	70°C,168hr,inWater	ASTM D471	1.0	%
				Volume change	24°C,168hr,inReferenceFuelB	ISO 1817	49	%
					Volume change	70°C,168hr,inASTM#1Oil	ISO 1817	5.0	%
						Volume change	70°C,168hr,inIRM903Oil	ISO 1817	42	%
						Volume change	Volume change	70°C,168hr,inWater	ISO 1817	1.0	%
Change rate of tensile strength in air	100°C,168hr	ASTM D573	41	%
	Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	-3.0	%
		Change rate of tensile strength in air	70°C,168hr	ISO 188	34	%
			Change rate of tensile strength in air	100%Strain70°C,168hr	ISO 188	5.0	%
				Change rate of tensile strength in air	100°C,168hr	ISO 188	41	%
				Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 188	-3.0	%
Change rate of ultimate elongation in air	70°C,168hr	ASTM D573	8.0	%
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	18	%
Tensile stress change rate	70°C,168hr，Break	ISO 1817	8.0	%
Tensile stress change rate	Tensile stress change rate	100°C,168hr，Break	ISO 1817	18	%
Change rate of tensile strength in air	70°C,168hr	ASTM D573	34	%
Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain,70°C,168hr	ASTM D573	5.0	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.