PA66 Huafon EP158N
211
- Properties:wear resistantLow temperature resistancHigh impact resistanceHigh tensile strengthGood resilienceGood impact resistance anSelf lubrication and wear
- Usages:Mechanical componentsElectronic fieldElectrical fieldInstrumentationAutomotive sectorrailwayHome appliance industrycommunicationTextileOil pipePrecision engineering productsfilmpacking materialMedical devicessporting goodsDaily necessities
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| relative viscosity | QB | 2.57±0.05 | |
| Terminal amino content | QB | 47±5 MEQ/KG | |
| water content | QB | ≤2000 ppm | |
| QB | ≤3000 ppm | ||
| granularity | QB | 1.7±0.4 g/100pellets | |
| density | ISO 1183 | 1.14 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 80 cm3/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 5.38 kJ/m² | |
| ISO 179 | 3.93 kJ/m² | ||
| tensile strength | ISO 527 | 86.5 Mpa | |
| elongation | ISO 527 | 40.3 % | |
| Flexural modulus | ISO 178 | 3114 Mpa | |
| bending strength | ISO 178 | 119 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75 | 204 °C | |
| ISO 75 | 70.2 °C | ||
| UL flame retardant rating | UL 94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.