| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | JIS K-7112 | 1.08 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 2-6 10 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 0.2-0.3 % |
| melt mass-flow rate | | JIS K-7210 | 6.5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | JIS K-7203 | 1100 kg/cm |
| tensile strength | | JIS K-7113 | 820 kg/cm |
| elongation at break | | JIS K-7113 | 2.7 % |
| Impact strength of cantilever beam gap | | JIS K-7110 | 1.7 kg-cm/cm of notch |
| Rubbing modulus | | JIS K-7203 | 3.7 10 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D-257 | >10 Ω.cm |
| Rockwell hardness | | JIS K-7202 | 94 M Scale |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | JIS K-7206 | 105 °C |
| Heat distortion temperature | | JIS K-7207 | 95 °C |
| flammability | | UL 94 | HB |
| Linear coefficient of thermal expansion | | ASTM D-696 | 6.8 10 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.