ABS

ABS ESTADIENE 1016 HT V0 Cossa Polimeri S.r.l.

Usages:
Electrical and electronic application fields furniture engineering accessories
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D256	90 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	0°C	ASTM D256	70 J/m

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	960 °C
UL flame retardant rating	3.2mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ASTM D790	2700 MPa
elongation	Break	ASTM D638	5.0 %
tensile strength	Break	ASTM D638	43.0 MPa
tensile strength	tensile strength	Yield	ASTM D638	50.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ASTM D15252	123 °C
Ball pressure temperature		IEC 60335-1	105 °C
Vicat softening temperature	--	ASTM D15253	115 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ASTM D955	0.30to0.60 %
melt mass-flow rate	240°C/5.0kg	ASTM D1238	14 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	4.0 g/10min
density		ASTM D792	1.20 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.