Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Environmental stress cracking resistance | | hr | 1.00to1000 |
| Carbon black content | | % | 40to45 |
| Water absorption rate | | % | 9.8E-3-0.011 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 46to96 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | | 58to88 |
| Haze ratio | | % | 2.2to7.3 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | % | 30to32 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | kJ/m² | 62.679 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | % | 1.0to530 |
| Flexural modulus | | | 97.24to171.03 Mpa |
| yield | | % | 5.6to19 |
| fracture | | % | 36to830 |
| fracture | | | 10.69to26.76 Mpa |
| fracture | | | 12.0to19.17 Mpa |
| yield | | | 10.0to24.41 Mpa |
| yield | | | 10.76to27.45 Mpa |
| coefficient of friction | | | 0.10to0.50 |
| film | Test Condition | Test Method | Test Result |
|---|
| MD: Fracture | | | 20.69to60.69 Mpa |
| MD: Surrender | | | 4.8to20.34 Mpa |
| TD: Fracture | | % | 580to720 |
| Dart impact | | g | 55to110 |
| MD: Fracture | | % | 350to720 |
| TD: Fracture | | | 20.21to62.76 Mpa |
| film thickness | | mil | 0.90to1.8 |
| TD | | g | 220to600 |
| TD | | | 105.52to224.83 Mpa |
| TD: Yield | | | 4.2to11.03 Mpa |
| MD | | g | 100to360 |
| MD | | | 107.59to184.83 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | | 2.30to3.70 |
| Dissipation Factor | | | 3.0E-4到0.010 |
| Surface Resistivity | | ohms | 2.0到2.5E+13 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | °C | -75--48 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.