PA9T Genestar™ GW2458
212
- Properties:High mobilityLow warpageGlass fiber reinforced
- Usages:Laptop caseElectronic fieldElectrical field
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 84 g/10 min | |
| Shrinkage rate | 0.030 % | ||
| 0.40 % | |||
| Water absorption rate | 0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Bar Flow Length | 7.10 CM | ||
| elongation at break | ASTM D638 | 0.30 % | |
| Weld Strength | ASTM D638 | 35.0 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 165 Mpa | |
| elongation | ASTM D638 | 3.5 % | |
| Flexural modulus | ASTM D790 | 15000 Mpa | |
| bending strength | ASTM D790 | 225 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 30 KV/mm | |
| dielectric constant | ASTM D150 | 3.80 | |
| Dissipation Factor | ASTM D150 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 285 °C | |
| Glass Transition Temperature | 125 °C | ||
| melting temperature | 306 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.