Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.64 g/cm³ |
Shrinkage rate | | ASTM D955 | 0.25 % |
Shrinkage rate | | ASTM D955 | 0.32 % |
Shrinkage rate | | ASTM D955 | 0.53 % |
Shrinkage rate | | ASTM D955 | 0.79 % |
Water absorption rate | | ASTM D570 | 0.060 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | R-Scale | ASTM D785 | 113 |
flammability | Test Condition | Test Method | Test Result |
---|
burning rate | | ISO 3795 | 47 mm/min |
UL flame retardant rating | | UL 94 | HB |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
bending strength | | ISO 178 | 170 MPa |
compressive strength | | ASTM D695 | 151 MPa |
shear strength | | ASTM D732 | 59.0 MPa |
tensile strength | | ISO 527-2/5 | 111 MPa |
Flexural modulus | | ISO 178 | 10500 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180 | 6.7 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | ASTM D257 | 1.1E+15 ohms·cm |
dielectric strength | | ASTM D149 | 22 kV/mm |
dielectric strength | | ASTM D149 | 16 kV/mm |
dielectric constant | | ASTM D150 | 3.80 |
Dissipation Factor | | ASTM D150 | 0.011 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/A | 224 °C |
melting temperature | | ISO 11357-3 | 249 °C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 1.7E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 8.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.