PC GS2010MDR 9911A MITSUBISHI THAILAND

Form：Granules | Grade：Flame retardant enhanced grade

Properties:

enhanceFiller: Glass fiber reinf10%Filler by weight

Typical Applications:

Fiber gradeCamera applications

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Fiber grade \| Camera applications
Properties:	enhance \| Filler: Glass fiber reinf \| 10% \| Filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	55	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	135	Mpa
Bending modulus		ISO 178	4000	Mpa
Tensile strain	Break	ISO 527-2	2.9	%
tensile strength	Break	ISO 527-2	78.0	Mpa
Tensile modulus		ISO 527-2	4500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	6.7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	4E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	140	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	145	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C	ISO 62	0.14	%
Shrinkage rate	MD:3.20mm		0.30-0.50	%
Shrinkage rate	Shrinkage rate	TD:3.20mm		0.40-0.60	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.00	cm3/10min
melt mass-flow rate	300°C/1.2kg	ISO 1133	10	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	CTI	UL 746	PLC 4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.